Nickel 201 vs. R04295 Alloy

Nickel 201 belongs to the nickel alloys classification, while R04295 alloy belongs to the otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is nickel 201 and the bottom bar is R04295 alloy.

Nickel Alloy 201 (2.4068, N02201, NA12)UNS R04295 Niobium-Hafnium Alloy

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		180
Elastic (Young's, Tensile) Modulus, GPa		100

Elongation at Break, %		4.5 to 45
Elongation at Break, %		22

Poisson's Ratio		0.31
Poisson's Ratio		0.38

Shear Modulus, GPa		70
Shear Modulus, GPa		37

Tensile Strength: Ultimate (UTS), MPa		390 to 660
Tensile Strength: Ultimate (UTS), MPa		410

Tensile Strength: Yield (Proof), MPa		80 to 510
Tensile Strength: Yield (Proof), MPa		300

Thermal Properties

Latent Heat of Fusion, J/g		290
Latent Heat of Fusion, J/g		300

Specific Heat Capacity, J/kg-K		440
Specific Heat Capacity, J/kg-K		260

Thermal Expansion, µm/m-K		13
Thermal Expansion, µm/m-K		7.2

Otherwise Unclassified Properties

Density, g/cm³		8.9
Density, g/cm³		9.0

Embodied Water, L/kg		230
Embodied Water, L/kg		950

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m³		25 to 130
Resilience: Ultimate (Unit Rupture Work), MJ/m³		84

Resilience: Unit (Modulus of Resilience), kJ/m³		17 to 720
Resilience: Unit (Modulus of Resilience), kJ/m³		430

Stiffness to Weight: Axial, points		11
Stiffness to Weight: Axial, points		6.3

Stiffness to Weight: Bending, points		21
Stiffness to Weight: Bending, points		17

Strength to Weight: Axial, points		12 to 20
Strength to Weight: Axial, points		13

Strength to Weight: Bending, points		13 to 19
Strength to Weight: Bending, points		14

Thermal Shock Resistance, points		11 to 19
Thermal Shock Resistance, points		40

Alloy Composition

Carbon (C), %		0 to 0.020
Carbon (C), %		0 to 0.015

Copper (Cu), %		0 to 0.25
Copper (Cu), %		0

Hafnium (Hf), %		0
Hafnium (Hf), %		9.0 to 11

Hydrogen (H), %		0
Hydrogen (H), %		0 to 0.0015

Iron (Fe), %		0 to 0.4
Iron (Fe), %		0

Manganese (Mn), %		0 to 0.35
Manganese (Mn), %		0

Nickel (Ni), %		99 to 100
Nickel (Ni), %		0

Niobium (Nb), %		0
Niobium (Nb), %		85.9 to 90.3

Nitrogen (N), %		0
Nitrogen (N), %		0 to 0.010

Oxygen (O), %		0
Oxygen (O), %		0 to 0.025

Silicon (Si), %		0 to 0.35
Silicon (Si), %		0

Sulfur (S), %		0 to 0.010
Sulfur (S), %		0

Tantalum (Ta), %		0
Tantalum (Ta), %		0 to 0.5

Titanium (Ti), %		0
Titanium (Ti), %		0.7 to 1.3

Tungsten (W), %		0
Tungsten (W), %		0 to 0.5

Zirconium (Zr), %		0
Zirconium (Zr), %		0 to 0.7