Nickel 201 vs. R05240 Alloy

Nickel 201 belongs to the nickel alloys classification, while R05240 alloy belongs to the otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is nickel 201 and the bottom bar is R05240 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 180
150
Elongation at Break, % 4.5 to 45
25
Poisson's Ratio 0.31
0.36
Shear Modulus, GPa 70
57
Tensile Strength: Ultimate (UTS), MPa 390 to 660
270
Tensile Strength: Yield (Proof), MPa 80 to 510
170

Thermal Properties

Latent Heat of Fusion, J/g 290
210
Specific Heat Capacity, J/kg-K 440
190
Thermal Expansion, µm/m-K 13
6.8

Otherwise Unclassified Properties

Density, g/cm3 8.9
14
Embodied Water, L/kg 230
460

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 25 to 130
59
Resilience: Unit (Modulus of Resilience), kJ/m3 17 to 720
90
Stiffness to Weight: Axial, points 11
6.3
Stiffness to Weight: Bending, points 21
13
Strength to Weight: Axial, points 12 to 20
5.4
Strength to Weight: Bending, points 13 to 19
6.8
Thermal Shock Resistance, points 11 to 19
18

Alloy Composition

Carbon (C), % 0 to 0.020
0 to 0.010
Copper (Cu), % 0 to 0.25
0
Hydrogen (H), % 0
0 to 0.0015
Iron (Fe), % 0 to 0.4
0 to 0.010
Manganese (Mn), % 0 to 0.35
0
Molybdenum (Mo), % 0
0 to 0.020
Nickel (Ni), % 99 to 100
0 to 0.010
Niobium (Nb), % 0
35 to 42
Nitrogen (N), % 0
0 to 0.010
Oxygen (O), % 0
0 to 0.020
Silicon (Si), % 0 to 0.35
0 to 0.0050
Sulfur (S), % 0 to 0.010
0
Tantalum (Ta), % 0
57.9 to 65
Titanium (Ti), % 0
0 to 0.010
Tungsten (W), % 0
0 to 0.050