Nickel 30 belongs to the nickel alloys classification, while SAE-AISI 4024 steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is nickel 30 and the bottom bar is SAE-AISI 4024 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 34
14
Fatigue Strength, MPa 200
320
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 82
73
Shear Strength, MPa 440
370
Tensile Strength: Ultimate (UTS), MPa 660
600
Tensile Strength: Yield (Proof), MPa 270
500

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Maximum Temperature: Mechanical, °C 1020
400
Melting Completion (Liquidus), °C 1480
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 10
51
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.5
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 1.6
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 60
2.1
Density, g/cm3 8.5
7.8
Embodied Carbon, kg CO2/kg material 9.4
1.5
Embodied Energy, MJ/kg 130
19
Embodied Water, L/kg 290
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
77
Resilience: Unit (Modulus of Resilience), kJ/m3 180
670
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 22
21
Strength to Weight: Bending, points 20
20
Thermal Diffusivity, mm2/s 2.7
14
Thermal Shock Resistance, points 18
18

Alloy Composition

Carbon (C), % 0 to 0.030
0.2 to 0.25
Chromium (Cr), % 28 to 31.5
0
Cobalt (Co), % 0 to 5.0
0
Copper (Cu), % 1.0 to 2.4
0
Iron (Fe), % 13 to 17
98.1 to 98.7
Manganese (Mn), % 0 to 0.030
0.7 to 0.9
Molybdenum (Mo), % 4.0 to 6.0
0.2 to 0.3
Nickel (Ni), % 30.2 to 52.2
0
Niobium (Nb), % 0.3 to 1.5
0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 0.8
0.15 to 0.35
Sulfur (S), % 0 to 0.020
0.035 to 0.050
Tungsten (W), % 1.5 to 4.0
0