Nickel 601 vs. Grade 7 Babbitt Metal

Nickel 601 belongs to the nickel alloys classification, while grade 7 Babbitt Metal belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is nickel 601 and the bottom bar is grade 7 Babbitt Metal.

Nickel Alloy 601 (N06601, NA49)Grade 7 (L53585) Lead-Base Babbitt Metal

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		200
Elastic (Young's, Tensile) Modulus, GPa		26

Poisson's Ratio		0.28
Poisson's Ratio		0.4

Shear Modulus, GPa		76
Shear Modulus, GPa		9.1

Tensile Strength: Yield (Proof), MPa		290 to 800
Tensile Strength: Yield (Proof), MPa		25

Thermal Properties

Latent Heat of Fusion, J/g		320
Latent Heat of Fusion, J/g		48

Melting Completion (Liquidus), °C		1410
Melting Completion (Liquidus), °C		270

Melting Onset (Solidus), °C		1360
Melting Onset (Solidus), °C		240

Specific Heat Capacity, J/kg-K		470
Specific Heat Capacity, J/kg-K		150

Thermal Expansion, µm/m-K		14
Thermal Expansion, µm/m-K		26

Otherwise Unclassified Properties

Base Metal Price, % relative		49
Base Metal Price, % relative		23

Density, g/cm³		8.3
Density, g/cm³		10

Embodied Carbon, kg CO₂/kg material		8.0
Embodied Carbon, kg CO₂/kg material		4.4

Embodied Energy, MJ/kg		110
Embodied Energy, MJ/kg		62

Embodied Water, L/kg		280
Embodied Water, L/kg		880

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m³		210 to 1630
Resilience: Unit (Modulus of Resilience), kJ/m³		12

Stiffness to Weight: Axial, points		13
Stiffness to Weight: Axial, points		1.4

Stiffness to Weight: Bending, points		23
Stiffness to Weight: Bending, points		9.6

Alloy Composition

Aluminum (Al), %		1.0 to 1.7
Aluminum (Al), %		0 to 0.0050

Antimony (Sb), %		0
Antimony (Sb), %		14 to 16

Arsenic (As), %		0
Arsenic (As), %		0.3 to 0.6

Bismuth (Bi), %		0
Bismuth (Bi), %		0 to 0.1

Cadmium (Cd), %		0
Cadmium (Cd), %		0 to 0.050

Carbon (C), %		0 to 0.1
Carbon (C), %		0

Chromium (Cr), %		21 to 25
Chromium (Cr), %		0

Copper (Cu), %		0 to 1.0
Copper (Cu), %		0 to 0.5

Iron (Fe), %		7.7 to 20
Iron (Fe), %		0 to 0.1

Lead (Pb), %		0
Lead (Pb), %		71.9 to 76.4

Manganese (Mn), %		0 to 1.0
Manganese (Mn), %		0

Nickel (Ni), %		58 to 63
Nickel (Ni), %		0

Silicon (Si), %		0 to 0.5
Silicon (Si), %		0

Sulfur (S), %		0 to 0.015
Sulfur (S), %		0

Tin (Sn), %		0
Tin (Sn), %		9.3 to 10.7

Zinc (Zn), %		0
Zinc (Zn), %		0 to 0.0050