Nickel 601 vs. SAE-AISI 52100 Steel
Nickel 601 belongs to the nickel alloys classification, while SAE-AISI 52100 steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is nickel 601 and the bottom bar is SAE-AISI 52100 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 10 to 38 | |
| 10 to 20 |
| Fatigue Strength, MPa | 220 to 380 | |
| 250 to 340 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 76 | |
| 72 |
| Shear Strength, MPa | 440 to 530 | |
| 370 to 420 |
| Tensile Strength: Ultimate (UTS), MPa | 660 to 890 | |
| 590 to 2010 |
| Tensile Strength: Yield (Proof), MPa | 290 to 800 | |
| 360 to 560 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 1100 | |
| 430 |
| Melting Completion (Liquidus), °C | 1410 | |
| 1450 |
| Melting Onset (Solidus), °C | 1360 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 11 | |
| 47 |
| Thermal Expansion, µm/m-K | 14 | |
| 12 to 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.5 | |
| 7.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.6 | |
| 8.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 49 | |
| 2.4 |
| Density, g/cm3 | 8.3 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 8.0 | |
| 1.5 |
| Embodied Energy, MJ/kg | 110 | |
| 20 |
| Embodied Water, L/kg | 280 | |
| 51 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 86 to 200 | |
| 54 to 310 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 210 to 1630 | |
| 350 to 840 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 22 to 30 | |
| 21 to 72 |
| Strength to Weight: Bending, points | 20 to 25 | |
| 20 to 45 |
| Thermal Diffusivity, mm2/s | 2.8 | |
| 13 |
| Thermal Shock Resistance, points | 17 to 23 | |
| 19 to 61 |
Alloy Composition
| Aluminum (Al), % | 1.0 to 1.7 | |
| 0 |
| Carbon (C), % | 0 to 0.1 | |
| 0.93 to 1.1 |
| Chromium (Cr), % | 21 to 25 | |
| 1.4 to 1.6 |
| Copper (Cu), % | 0 to 1.0 | |
| 0 |
| Iron (Fe), % | 7.7 to 20 | |
| 96.5 to 97.3 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.25 to 0.45 |
| Nickel (Ni), % | 58 to 63 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.5 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.015 |