Nickel 601 vs. K94200 Alloy
Nickel 601 belongs to the nickel alloys classification, while K94200 alloy belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is nickel 601 and the bottom bar is K94200 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 140 |
| Elongation at Break, % | 10 to 38 | |
| 5.0 to 32 |
| Poisson's Ratio | 0.28 | |
| 0.34 |
| Shear Modulus, GPa | 76 | |
| 54 |
| Shear Strength, MPa | 440 to 530 | |
| 330 to 410 |
| Tensile Strength: Ultimate (UTS), MPa | 660 to 890 | |
| 500 to 710 |
| Tensile Strength: Yield (Proof), MPa | 290 to 800 | |
| 270 to 650 |
Thermal Properties
| Curie Temperature, °C | -200 | |
| 350 |
| Melting Onset (Solidus), °C | 1360 | |
| 1440 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 500 |
| Thermal Conductivity, W/m-K | 11 | |
| 15 |
| Thermal Expansion, µm/m-K | 14 | |
| 5.0 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.5 | |
| 2.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.6 | |
| 3.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.3 | |
| 8.2 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 86 to 200 | |
| 35 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 210 to 1630 | |
| 250 to 1460 |
| Stiffness to Weight: Axial, points | 13 | |
| 9.8 |
| Stiffness to Weight: Bending, points | 23 | |
| 21 |
| Strength to Weight: Axial, points | 22 to 30 | |
| 17 to 24 |
| Strength to Weight: Bending, points | 20 to 25 | |
| 17 to 22 |
| Thermal Diffusivity, mm2/s | 2.8 | |
| 3.7 |
| Thermal Shock Resistance, points | 17 to 23 | |
| 49 to 70 |