Nickel 617 vs. SAE-AISI M62 Steel

Nickel 617 belongs to the nickel alloys classification, while SAE-AISI M62 steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is nickel 617 and the bottom bar is SAE-AISI M62 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 80
79
Tensile Strength: Ultimate (UTS), MPa 740
830 to 2440

Thermal Properties

Latent Heat of Fusion, J/g 330
260
Melting Completion (Liquidus), °C 1380
1650
Melting Onset (Solidus), °C 1330
1600
Specific Heat Capacity, J/kg-K 450
430
Thermal Expansion, µm/m-K 12
12

Otherwise Unclassified Properties

Base Metal Price, % relative 75
30
Density, g/cm3 8.5
8.5
Embodied Carbon, kg CO2/kg material 10
10
Embodied Energy, MJ/kg 140
150
Embodied Water, L/kg 350
110

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 23
23
Strength to Weight: Axial, points 24
27 to 80
Strength to Weight: Bending, points 21
23 to 47
Thermal Shock Resistance, points 21
24 to 71

Alloy Composition

Aluminum (Al), % 0.8 to 1.5
0
Boron (B), % 0 to 0.0060
0
Carbon (C), % 0.050 to 0.15
1.3 to 1.4
Chromium (Cr), % 20 to 24
3.5 to 4.0
Cobalt (Co), % 10 to 15
0
Copper (Cu), % 0 to 0.5
0 to 0.25
Iron (Fe), % 0 to 3.0
73.6 to 77.4
Manganese (Mn), % 0 to 1.0
0.15 to 0.4
Molybdenum (Mo), % 8.0 to 10
10 to 11
Nickel (Ni), % 44.5 to 62
0 to 0.3
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 1.0
0.15 to 0.4
Sulfur (S), % 0 to 0.015
0 to 0.030
Tungsten (W), % 0
5.8 to 6.5
Vanadium (V), % 0
1.8 to 2.1