Nickel 625 vs. 88-silver 12-tin-oxide
Nickel 625 belongs to the nickel alloys classification, while 88-silver 12-tin-oxide belongs to the otherwise unclassified metals. There are 6 material properties with values for both materials. Properties with values for just one material (25, in this case) are not shown.
For each property being compared, the top bar is nickel 625 and the bottom bar is 88-silver 12-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.3 | |
| 84 to 86 |
| Elongation at Break, % | 33 to 34 | |
| 9.0 to 37 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 220 to 250 | |
| 24 to 70 |
| Shear Strength, MPa | 530 to 600 | |
| 150 to 160 |
| Tensile Strength: Ultimate (UTS), MPa | 790 to 910 | |
| 230 to 280 |
| Tensile Strength: Yield (Proof), MPa | 320 to 450 | |
| 110 to 260 |