Nickel 625 vs. EN 2.4951 Nickel

Both nickel 625 and EN 2.4951 nickel are nickel alloys. They have 87% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is nickel 625 and the bottom bar is EN 2.4951 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 33 to 34
34
Fatigue Strength, MPa 240 to 320
200
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 79
76
Shear Strength, MPa 530 to 600
500
Tensile Strength: Ultimate (UTS), MPa 790 to 910
750
Tensile Strength: Yield (Proof), MPa 320 to 450
270

Thermal Properties

Latent Heat of Fusion, J/g 330
320
Maximum Temperature: Mechanical, °C 980
1150
Melting Completion (Liquidus), °C 1350
1360
Melting Onset (Solidus), °C 1290
1310
Specific Heat Capacity, J/kg-K 440
460
Thermal Conductivity, W/m-K 11
12
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.3
1.6
Electrical Conductivity: Equal Weight (Specific), % IACS 1.4
1.7

Otherwise Unclassified Properties

Base Metal Price, % relative 80
60
Density, g/cm3 8.6
8.5
Embodied Carbon, kg CO2/kg material 14
9.3
Embodied Energy, MJ/kg 190
130
Embodied Water, L/kg 290
280

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 220 to 250
200
Resilience: Unit (Modulus of Resilience), kJ/m3 260 to 490
190
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 23
23
Strength to Weight: Axial, points 26 to 29
25
Strength to Weight: Bending, points 22 to 24
22
Thermal Diffusivity, mm2/s 2.9
3.1
Thermal Shock Resistance, points 22 to 25
23

Alloy Composition

Aluminum (Al), % 0 to 0.4
0 to 0.3
Carbon (C), % 0 to 0.1
0.080 to 0.15
Chromium (Cr), % 20 to 23
18 to 21
Cobalt (Co), % 0 to 1.0
0 to 5.0
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 0 to 5.0
0 to 5.0
Manganese (Mn), % 0 to 0.5
0 to 1.0
Molybdenum (Mo), % 8.0 to 10
0
Nickel (Ni), % 58 to 68.9
65.4 to 81.7
Niobium (Nb), % 3.2 to 4.2
0
Phosphorus (P), % 0 to 0.015
0 to 0.020
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.015
Titanium (Ti), % 0 to 0.4
0.2 to 0.6