Nickel 684 vs. AWS ERNiCrCoMo-1
Both nickel 684 and AWS ERNiCrCoMo-1 are nickel alloys. They have 90% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is nickel 684 and the bottom bar is AWS ERNiCrCoMo-1.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 210 |
| Elongation at Break, % | 11 | |
| 28 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 76 | |
| 81 |
| Tensile Strength: Ultimate (UTS), MPa | 1190 | |
| 710 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 330 |
| Melting Completion (Liquidus), °C | 1370 | |
| 1420 |
| Melting Onset (Solidus), °C | 1320 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 450 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 75 | |
| 75 |
| Density, g/cm3 | 8.3 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 10 | |
| 10 |
| Embodied Energy, MJ/kg | 140 | |
| 140 |
| Embodied Water, L/kg | 360 | |
| 350 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 23 |
| Strength to Weight: Axial, points | 40 | |
| 23 |
| Strength to Weight: Bending, points | 30 | |
| 21 |
| Thermal Shock Resistance, points | 34 | |
| 19 |
Alloy Composition
| Aluminum (Al), % | 2.5 to 3.3 | |
| 0.8 to 1.5 |
| Boron (B), % | 0.0030 to 0.010 | |
| 0 |
| Carbon (C), % | 0 to 0.15 | |
| 0.050 to 0.15 |
| Chromium (Cr), % | 15 to 20 | |
| 20 to 24 |
| Cobalt (Co), % | 13 to 20 | |
| 10 to 15 |
| Copper (Cu), % | 0 to 0.15 | |
| 0 to 0.5 |
| Iron (Fe), % | 0 to 4.0 | |
| 0 to 3.0 |
| Manganese (Mn), % | 0 to 0.75 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 3.0 to 5.0 | |
| 8.0 to 10 |
| Nickel (Ni), % | 42.7 to 64 | |
| 42.7 to 61.2 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.75 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.015 |
| Titanium (Ti), % | 2.5 to 3.3 | |
| 0 to 0.6 |
| Residuals, % | 0 | |
| 0 to 0.5 |