Nickel 685 vs. ASTM A182 Grade F10
Nickel 685 belongs to the nickel alloys classification, while ASTM A182 grade F10 belongs to the iron alloys. They have a modest 30% of their average alloy composition in common, which, by itself, doesn't mean much. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is nickel 685 and the bottom bar is ASTM A182 grade F10.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 350 | |
| 190 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 17 | |
| 34 |
| Fatigue Strength, MPa | 470 | |
| 180 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Reduction in Area, % | 20 | |
| 56 |
| Shear Modulus, GPa | 77 | |
| 74 |
| Shear Strength, MPa | 770 | |
| 420 |
| Tensile Strength: Ultimate (UTS), MPa | 1250 | |
| 630 |
| Tensile Strength: Yield (Proof), MPa | 850 | |
| 230 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 290 |
| Maximum Temperature: Mechanical, °C | 1000 | |
| 600 |
| Melting Completion (Liquidus), °C | 1380 | |
| 1420 |
| Melting Onset (Solidus), °C | 1330 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 470 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 75 | |
| 18 |
| Density, g/cm3 | 8.4 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 10 | |
| 3.6 |
| Embodied Energy, MJ/kg | 140 | |
| 51 |
| Embodied Water, L/kg | 340 | |
| 120 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 190 | |
| 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1820 | |
| 140 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 42 | |
| 22 |
| Strength to Weight: Bending, points | 31 | |
| 21 |
| Thermal Shock Resistance, points | 37 | |
| 18 |
Alloy Composition
| Aluminum (Al), % | 1.2 to 1.6 | |
| 0 |
| Boron (B), % | 0.0030 to 0.010 | |
| 0 |
| Carbon (C), % | 0.030 to 0.1 | |
| 0.1 to 0.2 |
| Chromium (Cr), % | 18 to 21 | |
| 7.0 to 9.0 |
| Cobalt (Co), % | 12 to 15 | |
| 0 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 |
| Iron (Fe), % | 0 to 2.0 | |
| 66.5 to 72.4 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.5 to 0.8 |
| Molybdenum (Mo), % | 3.5 to 5.0 | |
| 0 |
| Nickel (Ni), % | 49.6 to 62.5 | |
| 19 to 22 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.75 | |
| 1.0 to 1.4 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Titanium (Ti), % | 2.8 to 3.3 | |
| 0 |
| Zinc (Zn), % | 0.020 to 0.12 | |
| 0 |