Nickel 685 vs. EN 1.3558 Steel
Nickel 685 belongs to the nickel alloys classification, while EN 1.3558 steel belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is nickel 685 and the bottom bar is EN 1.3558 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 350 | |
| 230 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 210 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 1250 | |
| 770 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 240 |
| Maximum Temperature: Mechanical, °C | 1000 | |
| 490 |
| Melting Completion (Liquidus), °C | 1380 | |
| 1810 |
| Melting Onset (Solidus), °C | 1330 | |
| 1760 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 410 |
| Thermal Conductivity, W/m-K | 13 | |
| 20 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 75 | |
| 45 |
| Density, g/cm3 | 8.4 | |
| 9.3 |
| Embodied Carbon, kg CO2/kg material | 10 | |
| 8.4 |
| Embodied Energy, MJ/kg | 140 | |
| 130 |
| Embodied Water, L/kg | 340 | |
| 90 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 12 |
| Stiffness to Weight: Bending, points | 23 | |
| 21 |
| Strength to Weight: Axial, points | 42 | |
| 23 |
| Strength to Weight: Bending, points | 31 | |
| 20 |
| Thermal Diffusivity, mm2/s | 3.3 | |
| 5.3 |
| Thermal Shock Resistance, points | 37 | |
| 22 |
Alloy Composition
| Aluminum (Al), % | 1.2 to 1.6 | |
| 0 |
| Boron (B), % | 0.0030 to 0.010 | |
| 0 |
| Carbon (C), % | 0.030 to 0.1 | |
| 0.7 to 0.8 |
| Chromium (Cr), % | 18 to 21 | |
| 3.9 to 4.3 |
| Cobalt (Co), % | 12 to 15 | |
| 0 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 to 0.3 |
| Iron (Fe), % | 0 to 2.0 | |
| 73.7 to 77.6 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 0.4 |
| Molybdenum (Mo), % | 3.5 to 5.0 | |
| 0 to 0.6 |
| Nickel (Ni), % | 49.6 to 62.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.75 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.015 |
| Titanium (Ti), % | 2.8 to 3.3 | |
| 0 |
| Tungsten (W), % | 0 | |
| 17.5 to 19 |
| Vanadium (V), % | 0 | |
| 1.0 to 1.3 |
| Zinc (Zn), % | 0.020 to 0.12 | |
| 0 |