Nickel 685 vs. SAE-AISI 1046 Steel
Nickel 685 belongs to the nickel alloys classification, while SAE-AISI 1046 steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is nickel 685 and the bottom bar is SAE-AISI 1046 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 350 | |
| 190 to 210 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 17 | |
| 14 to 17 |
| Fatigue Strength, MPa | 470 | |
| 240 to 390 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Reduction in Area, % | 20 | |
| 39 to 50 |
| Shear Modulus, GPa | 77 | |
| 72 |
| Shear Strength, MPa | 770 | |
| 410 to 450 |
| Tensile Strength: Ultimate (UTS), MPa | 1250 | |
| 660 to 740 |
| Tensile Strength: Yield (Proof), MPa | 850 | |
| 370 to 610 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 1000 | |
| 400 |
| Melting Completion (Liquidus), °C | 1380 | |
| 1460 |
| Melting Onset (Solidus), °C | 1330 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 470 |
| Thermal Conductivity, W/m-K | 13 | |
| 51 |
| Thermal Expansion, µm/m-K | 12 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 75 | |
| 1.8 |
| Density, g/cm3 | 8.4 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 10 | |
| 1.4 |
| Embodied Energy, MJ/kg | 140 | |
| 18 |
| Embodied Water, L/kg | 340 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 190 | |
| 91 to 95 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1820 | |
| 360 to 990 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 42 | |
| 23 to 26 |
| Strength to Weight: Bending, points | 31 | |
| 22 to 23 |
| Thermal Diffusivity, mm2/s | 3.3 | |
| 14 |
| Thermal Shock Resistance, points | 37 | |
| 23 to 25 |
Alloy Composition
| Aluminum (Al), % | 1.2 to 1.6 | |
| 0 |
| Boron (B), % | 0.0030 to 0.010 | |
| 0 |
| Carbon (C), % | 0.030 to 0.1 | |
| 0.43 to 0.5 |
| Chromium (Cr), % | 18 to 21 | |
| 0 |
| Cobalt (Co), % | 12 to 15 | |
| 0 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 |
| Iron (Fe), % | 0 to 2.0 | |
| 98.4 to 98.9 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.7 to 1.0 |
| Molybdenum (Mo), % | 3.5 to 5.0 | |
| 0 |
| Nickel (Ni), % | 49.6 to 62.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.75 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.050 |
| Titanium (Ti), % | 2.8 to 3.3 | |
| 0 |
| Zinc (Zn), % | 0.020 to 0.12 | |
| 0 |