Nickel 690 vs. C38000 Brass
Nickel 690 belongs to the nickel alloys classification, while C38000 brass belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is nickel 690 and the bottom bar is C38000 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 100 |
| Elongation at Break, % | 3.4 to 34 | |
| 17 |
| Poisson's Ratio | 0.28 | |
| 0.31 |
| Shear Modulus, GPa | 79 | |
| 39 |
| Shear Strength, MPa | 420 to 570 | |
| 230 |
| Tensile Strength: Ultimate (UTS), MPa | 640 to 990 | |
| 380 |
| Tensile Strength: Yield (Proof), MPa | 250 to 760 | |
| 120 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 1010 | |
| 110 |
| Melting Completion (Liquidus), °C | 1380 | |
| 800 |
| Melting Onset (Solidus), °C | 1340 | |
| 760 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 380 |
| Thermal Conductivity, W/m-K | 14 | |
| 110 |
| Thermal Expansion, µm/m-K | 14 | |
| 21 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 50 | |
| 22 |
| Density, g/cm3 | 8.3 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 8.2 | |
| 2.7 |
| Embodied Energy, MJ/kg | 120 | |
| 46 |
| Embodied Water, L/kg | 290 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 31 to 170 | |
| 50 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 160 to 1440 | |
| 74 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 21 to 33 | |
| 13 |
| Strength to Weight: Bending, points | 20 to 27 | |
| 14 |
| Thermal Diffusivity, mm2/s | 3.5 | |
| 37 |
| Thermal Shock Resistance, points | 16 to 25 | |
| 13 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.5 |
| Carbon (C), % | 0 to 0.050 | |
| 0 |
| Chromium (Cr), % | 27 to 31 | |
| 0 |
| Copper (Cu), % | 0 to 0.5 | |
| 55 to 60 |
| Iron (Fe), % | 7.0 to 11 | |
| 0 to 0.35 |
| Lead (Pb), % | 0 | |
| 1.5 to 2.5 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 |
| Nickel (Ni), % | 58 to 66 | |
| 0 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.3 |
| Zinc (Zn), % | 0 | |
| 35.9 to 43.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |