Nickel 718 vs. Class 4 Tungsten
Nickel 718 belongs to the nickel alloys classification, while class 4 tungsten belongs to the otherwise unclassified metals. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is nickel 718 and the bottom bar is class 4 tungsten.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 270 |
| Elongation at Break, % | 12 to 50 | |
| 2.3 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Rockwell C Hardness | 40 | |
| 31 |
| Shear Modulus, GPa | 75 | |
| 110 |
| Tensile Strength: Ultimate (UTS), MPa | 930 to 1530 | |
| 790 |
| Tensile Strength: Yield (Proof), MPa | 510 to 1330 | |
| 580 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 170 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 130 |
| Thermal Conductivity, W/m-K | 11 | |
| 30 |
| Thermal Expansion, µm/m-K | 13 | |
| 4.5 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.4 | |
| 17 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.5 | |
| 9.7 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.3 | |
| 16 |
| Embodied Carbon, kg CO2/kg material | 13 | |
| 24 |
| Embodied Energy, MJ/kg | 190 | |
| 360 |
| Embodied Water, L/kg | 250 | |
| 150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 to 390 | |
| 16 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 660 to 4560 | |
| 620 |
| Stiffness to Weight: Axial, points | 13 | |
| 9.6 |
| Stiffness to Weight: Bending, points | 23 | |
| 14 |
| Strength to Weight: Axial, points | 31 to 51 | |
| 14 |
| Strength to Weight: Bending, points | 25 to 35 | |
| 12 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 15 |
| Thermal Shock Resistance, points | 27 to 44 | |
| 46 |
Alloy Composition
| Aluminum (Al), % | 0.2 to 0.8 | |
| 0 |
| Boron (B), % | 0 to 0.0060 | |
| 0 |
| Carbon (C), % | 0 to 0.080 | |
| 0 |
| Chromium (Cr), % | 17 to 21 | |
| 0 |
| Cobalt (Co), % | 0 to 1.0 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 |
| Iron (Fe), % | 11.1 to 24.6 | |
| 0 |
| Manganese (Mn), % | 0 to 0.35 | |
| 0 |
| Molybdenum (Mo), % | 2.8 to 3.3 | |
| 0 |
| Nickel (Ni), % | 50 to 55 | |
| 0 |
| Niobium (Nb), % | 4.8 to 5.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 |
| Silicon (Si), % | 0 to 0.35 | |
| 0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Titanium (Ti), % | 0.65 to 1.2 | |
| 0 |
| Tungsten (W), % | 0 | |
| 97 |
| Residuals, % | 0 | |
| 3.0 |