Nickel 718 vs. SAE-AISI A4 Steel
Nickel 718 belongs to the nickel alloys classification, while SAE-AISI A4 steel belongs to the iron alloys. They have a modest 21% of their average alloy composition in common, which, by itself, doesn't mean much. There are 23 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is nickel 718 and the bottom bar is SAE-AISI A4 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 75 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 930 to 1530 | |
| 710 to 2050 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 250 |
| Melting Completion (Liquidus), °C | 1340 | |
| 1450 |
| Melting Onset (Solidus), °C | 1260 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 470 |
| Thermal Conductivity, W/m-K | 11 | |
| 40 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.4 | |
| 7.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.5 | |
| 8.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 75 | |
| 3.9 |
| Density, g/cm3 | 8.3 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 13 | |
| 1.8 |
| Embodied Energy, MJ/kg | 190 | |
| 24 |
| Embodied Water, L/kg | 250 | |
| 59 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 31 to 51 | |
| 25 to 73 |
| Strength to Weight: Bending, points | 25 to 35 | |
| 23 to 46 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 11 |
| Thermal Shock Resistance, points | 27 to 44 | |
| 23 to 67 |
Alloy Composition
| Aluminum (Al), % | 0.2 to 0.8 | |
| 0 |
| Boron (B), % | 0 to 0.0060 | |
| 0 |
| Carbon (C), % | 0 to 0.080 | |
| 1.0 to 1.1 |
| Chromium (Cr), % | 17 to 21 | |
| 0.9 to 2.2 |
| Cobalt (Co), % | 0 to 1.0 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 to 0.25 |
| Iron (Fe), % | 11.1 to 24.6 | |
| 92 to 95.5 |
| Manganese (Mn), % | 0 to 0.35 | |
| 1.8 to 2.2 |
| Molybdenum (Mo), % | 2.8 to 3.3 | |
| 0.9 to 1.4 |
| Nickel (Ni), % | 50 to 55 | |
| 0 to 0.3 |
| Niobium (Nb), % | 4.8 to 5.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.35 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.030 |
| Titanium (Ti), % | 0.65 to 1.2 | |
| 0 |