Nickel 80A vs. AWS E90C-D2

Nickel 80A belongs to the nickel alloys classification, while AWS E90C-D2 belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is nickel 80A and the bottom bar is AWS E90C-D2.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 22
19
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Tensile Strength: Ultimate (UTS), MPa 1040
690
Tensile Strength: Yield (Proof), MPa 710
620

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Melting Completion (Liquidus), °C 1360
1460
Melting Onset (Solidus), °C 1310
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 11
49
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.5
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 1.6
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 55
2.5
Density, g/cm3 8.3
7.8
Embodied Carbon, kg CO2/kg material 9.8
1.6
Embodied Energy, MJ/kg 140
21
Embodied Water, L/kg 280
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
130
Resilience: Unit (Modulus of Resilience), kJ/m3 1300
1010
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 35
25
Strength to Weight: Bending, points 27
22
Thermal Diffusivity, mm2/s 2.9
13
Thermal Shock Resistance, points 31
20

Alloy Composition

Aluminum (Al), % 0.5 to 1.8
0
Carbon (C), % 0 to 0.1
0 to 0.12
Chromium (Cr), % 18 to 21
0
Copper (Cu), % 0
0 to 0.35
Iron (Fe), % 0 to 3.0
95.5 to 98.6
Manganese (Mn), % 0 to 1.0
1.0 to 1.9
Molybdenum (Mo), % 0
0.4 to 0.6
Nickel (Ni), % 69.4 to 79.7
0
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.9
Sulfur (S), % 0 to 0.015
0 to 0.030
Titanium (Ti), % 1.8 to 2.7
0
Vanadium (V), % 0
0 to 0.030
Residuals, % 0
0 to 0.5