Nickel 80A vs. EN 1.1122 Steel

Nickel 80A belongs to the nickel alloys classification, while EN 1.1122 steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is nickel 80A and the bottom bar is EN 1.1122 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 22
12 to 21
Fatigue Strength, MPa 430
170 to 260
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Shear Strength, MPa 660
240 to 290
Tensile Strength: Ultimate (UTS), MPa 1040
340 to 460
Tensile Strength: Yield (Proof), MPa 710
240 to 370

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Maximum Temperature: Mechanical, °C 980
400
Melting Completion (Liquidus), °C 1360
1460
Melting Onset (Solidus), °C 1310
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 11
51
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.5
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 1.6
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 55
1.8
Density, g/cm3 8.3
7.9
Embodied Carbon, kg CO2/kg material 9.8
1.4
Embodied Energy, MJ/kg 140
18
Embodied Water, L/kg 280
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
36 to 89
Resilience: Unit (Modulus of Resilience), kJ/m3 1300
160 to 360
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 35
12 to 16
Strength to Weight: Bending, points 27
14 to 17
Thermal Diffusivity, mm2/s 2.9
14
Thermal Shock Resistance, points 31
11 to 15

Alloy Composition

Aluminum (Al), % 0.5 to 1.8
0
Carbon (C), % 0 to 0.1
0.080 to 0.12
Chromium (Cr), % 18 to 21
0
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 0 to 3.0
98.7 to 99.62
Manganese (Mn), % 0 to 1.0
0.3 to 0.6
Nickel (Ni), % 69.4 to 79.7
0
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.3
Sulfur (S), % 0 to 0.015
0 to 0.025
Titanium (Ti), % 1.8 to 2.7
0