Nickel 80A vs. EN 1.4005 Stainless Steel

Nickel 80A belongs to the nickel alloys classification, while EN 1.4005 stainless steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is nickel 80A and the bottom bar is EN 1.4005 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 22
13 to 21
Fatigue Strength, MPa 430
240 to 290
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
76
Shear Strength, MPa 660
390 to 450
Tensile Strength: Ultimate (UTS), MPa 1040
630 to 750
Tensile Strength: Yield (Proof), MPa 710
370 to 500

Thermal Properties

Latent Heat of Fusion, J/g 320
270
Maximum Temperature: Mechanical, °C 980
760
Melting Completion (Liquidus), °C 1360
1440
Melting Onset (Solidus), °C 1310
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 11
30
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.5
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 1.6
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 55
7.0
Density, g/cm3 8.3
7.7
Embodied Carbon, kg CO2/kg material 9.8
2.0
Embodied Energy, MJ/kg 140
28
Embodied Water, L/kg 280
100

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
90 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 1300
350 to 650
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 35
23 to 27
Strength to Weight: Bending, points 27
21 to 24
Thermal Diffusivity, mm2/s 2.9
8.1
Thermal Shock Resistance, points 31
23 to 27

Alloy Composition

Aluminum (Al), % 0.5 to 1.8
0
Carbon (C), % 0 to 0.1
0.060 to 0.15
Chromium (Cr), % 18 to 21
12 to 14
Iron (Fe), % 0 to 3.0
82.4 to 87.8
Manganese (Mn), % 0 to 1.0
0 to 1.5
Molybdenum (Mo), % 0
0 to 0.6
Nickel (Ni), % 69.4 to 79.7
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0.15 to 0.35
Titanium (Ti), % 1.8 to 2.7
0