Nickel 80A vs. N08535 Stainless Steel

Nickel 80A belongs to the nickel alloys classification, while N08535 stainless steel belongs to the iron alloys. They have 55% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is nickel 80A and the bottom bar is N08535 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 22
46
Fatigue Strength, MPa 430
220
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
80
Shear Strength, MPa 660
400
Tensile Strength: Ultimate (UTS), MPa 1040
570
Tensile Strength: Yield (Proof), MPa 710
240

Thermal Properties

Latent Heat of Fusion, J/g 320
310
Maximum Temperature: Mechanical, °C 980
1100
Melting Completion (Liquidus), °C 1360
1420
Melting Onset (Solidus), °C 1310
1370
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 11
13
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.5
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 1.6
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 55
36
Density, g/cm3 8.3
8.1
Embodied Carbon, kg CO2/kg material 9.8
6.3
Embodied Energy, MJ/kg 140
87
Embodied Water, L/kg 280
230

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
210
Resilience: Unit (Modulus of Resilience), kJ/m3 1300
140
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 35
20
Strength to Weight: Bending, points 27
19
Thermal Diffusivity, mm2/s 2.9
3.3
Thermal Shock Resistance, points 31
13

Alloy Composition

Aluminum (Al), % 0.5 to 1.8
0
Carbon (C), % 0 to 0.1
0 to 0.030
Chromium (Cr), % 18 to 21
24 to 27
Copper (Cu), % 0
0 to 1.5
Iron (Fe), % 0 to 3.0
29.4 to 44.5
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 0
2.5 to 4.0
Nickel (Ni), % 69.4 to 79.7
29 to 36.5
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.015
0 to 0.030
Titanium (Ti), % 1.8 to 2.7
0