Nickel 825 vs. EN 1.4466 Stainless Steel
Nickel 825 belongs to the nickel alloys classification, while EN 1.4466 stainless steel belongs to the iron alloys. They have 76% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is nickel 825 and the bottom bar is EN 1.4466 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Elongation at Break, % | 34 | |
| 42 |
| Fatigue Strength, MPa | 190 | |
| 250 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 78 | |
| 80 |
| Shear Strength, MPa | 430 | |
| 440 |
| Tensile Strength: Ultimate (UTS), MPa | 650 | |
| 640 |
| Tensile Strength: Yield (Proof), MPa | 260 | |
| 280 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 300 |
| Maximum Temperature: Mechanical, °C | 980 | |
| 1100 |
| Melting Completion (Liquidus), °C | 1400 | |
| 1420 |
| Melting Onset (Solidus), °C | 1370 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 470 |
| Thermal Conductivity, W/m-K | 11 | |
| 14 |
| Thermal Expansion, µm/m-K | 14 | |
| 16 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.5 | |
| 2.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.7 | |
| 2.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 41 | |
| 28 |
| Density, g/cm3 | 8.2 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 7.2 | |
| 5.0 |
| Embodied Energy, MJ/kg | 100 | |
| 70 |
| Embodied Water, L/kg | 230 | |
| 200 |
Common Calculations
| PREN (Pitting Resistance) | 31 | |
| 35 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 220 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 170 | |
| 200 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 22 | |
| 22 |
| Strength to Weight: Bending, points | 20 | |
| 21 |
| Thermal Diffusivity, mm2/s | 2.9 | |
| 3.7 |
| Thermal Shock Resistance, points | 17 | |
| 14 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.2 | |
| 0 |
| Carbon (C), % | 0 to 0.050 | |
| 0 to 0.020 |
| Chromium (Cr), % | 19.5 to 23.5 | |
| 24 to 26 |
| Copper (Cu), % | 1.5 to 3.0 | |
| 0 |
| Iron (Fe), % | 22 to 37.9 | |
| 45.6 to 52.9 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 2.5 to 3.5 | |
| 2.0 to 2.5 |
| Nickel (Ni), % | 38 to 46 | |
| 21 to 23 |
| Nitrogen (N), % | 0 | |
| 0.1 to 0.16 |
| Phosphorus (P), % | 0 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.050 | |
| 0 to 0.7 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0.6 to 1.2 | |
| 0 |