Nickel 890 vs. C10100 Copper

Nickel 890 belongs to the nickel alloys classification, while C10100 copper belongs to the copper alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is nickel 890 and the bottom bar is C10100 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
120
Elongation at Break, % 39
1.5 to 50
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 78
43
Shear Strength, MPa 400
150 to 240
Tensile Strength: Ultimate (UTS), MPa 590
220 to 410
Tensile Strength: Yield (Proof), MPa 230
69 to 400

Thermal Properties

Latent Heat of Fusion, J/g 330
210
Maximum Temperature: Mechanical, °C 1000
200
Melting Completion (Liquidus), °C 1390
1080
Melting Onset (Solidus), °C 1340
1080
Specific Heat Capacity, J/kg-K 480
390
Thermal Expansion, µm/m-K 14
17

Otherwise Unclassified Properties

Base Metal Price, % relative 47
31
Density, g/cm3 8.1
9.0
Embodied Carbon, kg CO2/kg material 8.2
2.6
Embodied Energy, MJ/kg 120
41
Embodied Water, L/kg 250
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
6.1 to 85
Resilience: Unit (Modulus of Resilience), kJ/m3 140
21 to 690
Stiffness to Weight: Axial, points 14
7.2
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 20
6.8 to 13
Strength to Weight: Bending, points 19
9.0 to 14
Thermal Shock Resistance, points 15
7.8 to 15

Alloy Composition

Aluminum (Al), % 0.050 to 0.6
0
Carbon (C), % 0.060 to 0.14
0
Chromium (Cr), % 23.5 to 28.5
0
Copper (Cu), % 0 to 0.75
99.99 to 100
Iron (Fe), % 17.3 to 33.9
0
Lead (Pb), % 0
0 to 0.0010
Manganese (Mn), % 0 to 1.5
0
Molybdenum (Mo), % 1.0 to 2.0
0
Nickel (Ni), % 40 to 45
0
Niobium (Nb), % 0.2 to 1.0
0
Oxygen (O), % 0
0 to 0.00050
Phosphorus (P), % 0
0 to 0.00030
Silicon (Si), % 1.0 to 2.0
0
Sulfur (S), % 0 to 0.015
0
Tantalum (Ta), % 0.1 to 0.6
0
Titanium (Ti), % 0.15 to 0.6
0
Zinc (Zn), % 0
0 to 0.00010