Nickel 908 vs. AISI 310 Stainless Steel
Nickel 908 belongs to the nickel alloys classification, while AISI 310 stainless steel belongs to the iron alloys. They have 66% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is nickel 908 and the bottom bar is AISI 310 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 180 | |
| 200 |
| Elongation at Break, % | 11 | |
| 34 to 45 |
| Fatigue Strength, MPa | 450 | |
| 240 to 280 |
| Poisson's Ratio | 0.3 | |
| 0.27 |
| Shear Modulus, GPa | 70 | |
| 78 |
| Shear Strength, MPa | 800 | |
| 420 to 470 |
| Tensile Strength: Ultimate (UTS), MPa | 1340 | |
| 600 to 710 |
| Tensile Strength: Yield (Proof), MPa | 930 | |
| 260 to 350 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 310 |
| Maximum Temperature: Mechanical, °C | 920 | |
| 1040 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1450 |
| Melting Onset (Solidus), °C | 1380 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 480 |
| Thermal Conductivity, W/m-K | 11 | |
| 15 |
| Thermal Expansion, µm/m-K | 8.6 | |
| 15 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 50 | |
| 25 |
| Density, g/cm3 | 8.3 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 9.3 | |
| 4.3 |
| Embodied Energy, MJ/kg | 140 | |
| 61 |
| Embodied Water, L/kg | 170 | |
| 190 |
Common Calculations
| PREN (Pitting Resistance) | 4.2 | |
| 25 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 | |
| 200 to 220 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2340 | |
| 170 to 310 |
| Stiffness to Weight: Axial, points | 12 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 25 |
| Strength to Weight: Axial, points | 45 | |
| 21 to 25 |
| Strength to Weight: Bending, points | 33 | |
| 20 to 22 |
| Thermal Diffusivity, mm2/s | 2.9 | |
| 3.9 |
| Thermal Shock Resistance, points | 61 | |
| 14 to 17 |
Alloy Composition
| Aluminum (Al), % | 0.75 to 1.3 | |
| 0 |
| Boron (B), % | 0 to 0.012 | |
| 0 |
| Carbon (C), % | 0 to 0.030 | |
| 0 to 0.25 |
| Chromium (Cr), % | 3.8 to 4.5 | |
| 24 to 26 |
| Cobalt (Co), % | 0 to 0.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 |
| Iron (Fe), % | 35.6 to 44.6 | |
| 48.2 to 57 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 2.0 |
| Nickel (Ni), % | 47 to 51 | |
| 19 to 22 |
| Niobium (Nb), % | 2.7 to 3.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 1.5 |
| Sulfur (S), % | 0 to 0.0050 | |
| 0 to 0.030 |
| Titanium (Ti), % | 1.2 to 1.8 | |
| 0 |