Nickel 908 vs. ASTM A369 Grade FP22
Nickel 908 belongs to the nickel alloys classification, while ASTM A369 grade FP22 belongs to the iron alloys. They have 43% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is nickel 908 and the bottom bar is ASTM A369 grade FP22.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 180 | |
| 190 |
| Elongation at Break, % | 11 | |
| 20 |
| Fatigue Strength, MPa | 450 | |
| 160 |
| Poisson's Ratio | 0.3 | |
| 0.29 |
| Shear Modulus, GPa | 70 | |
| 74 |
| Shear Strength, MPa | 800 | |
| 300 |
| Tensile Strength: Ultimate (UTS), MPa | 1340 | |
| 470 |
| Tensile Strength: Yield (Proof), MPa | 930 | |
| 240 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 920 | |
| 460 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1470 |
| Melting Onset (Solidus), °C | 1380 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 470 |
| Thermal Conductivity, W/m-K | 11 | |
| 39 |
| Thermal Expansion, µm/m-K | 8.6 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 50 | |
| 3.8 |
| Density, g/cm3 | 8.3 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 9.3 | |
| 1.7 |
| Embodied Energy, MJ/kg | 140 | |
| 23 |
| Embodied Water, L/kg | 170 | |
| 58 |
Common Calculations
| PREN (Pitting Resistance) | 4.2 | |
| 5.5 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 | |
| 80 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2340 | |
| 150 |
| Stiffness to Weight: Axial, points | 12 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 45 | |
| 17 |
| Strength to Weight: Bending, points | 33 | |
| 17 |
| Thermal Diffusivity, mm2/s | 2.9 | |
| 11 |
| Thermal Shock Resistance, points | 61 | |
| 14 |
Alloy Composition
| Aluminum (Al), % | 0.75 to 1.3 | |
| 0 |
| Boron (B), % | 0 to 0.012 | |
| 0 |
| Carbon (C), % | 0 to 0.030 | |
| 0.050 to 0.15 |
| Chromium (Cr), % | 3.8 to 4.5 | |
| 1.9 to 2.6 |
| Cobalt (Co), % | 0 to 0.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 |
| Iron (Fe), % | 35.6 to 44.6 | |
| 95 to 96.9 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.3 to 0.6 |
| Molybdenum (Mo), % | 0 | |
| 0.87 to 1.1 |
| Nickel (Ni), % | 47 to 51 | |
| 0 |
| Niobium (Nb), % | 2.7 to 3.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.0050 | |
| 0 to 0.025 |
| Titanium (Ti), % | 1.2 to 1.8 | |
| 0 |