Nickel Beryllium 360 vs. AISI 201 Stainless Steel

Nickel beryllium 360 belongs to the nickel alloys classification, while AISI 201 stainless steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is nickel beryllium 360 and the bottom bar is AISI 201 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 1.0 to 30
4.6 to 51
Fatigue Strength, MPa 260 to 710
280 to 600
Poisson's Ratio 0.3
0.28
Shear Modulus, GPa 77
77
Shear Strength, MPa 510 to 1100
450 to 840
Tensile Strength: Ultimate (UTS), MPa 780 to 1860
650 to 1450
Tensile Strength: Yield (Proof), MPa 380 to 1590
300 to 1080

Thermal Properties

Melting Completion (Liquidus), °C 1330
1410
Melting Onset (Solidus), °C 1200
1370
Specific Heat Capacity, J/kg-K 460
480
Thermal Conductivity, W/m-K 48
15
Thermal Expansion, µm/m-K 14
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 5.0
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 5.4
2.9

Otherwise Unclassified Properties

Density, g/cm3 8.3
7.7

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 12 to 190
61 to 340
Resilience: Unit (Modulus of Resilience), kJ/m3 360 to 3440
230 to 2970
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 26 to 62
23 to 52
Strength to Weight: Bending, points 23 to 41
22 to 37
Thermal Diffusivity, mm2/s 13
4.0
Thermal Shock Resistance, points 19 to 46
14 to 32

Comparable Variants