Nickel Beryllium 360 vs. ASTM A204 Steel
Nickel beryllium 360 belongs to the nickel alloys classification, while ASTM A204 steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is nickel beryllium 360 and the bottom bar is ASTM A204 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 1.0 to 30 | |
| 18 to 22 |
| Fatigue Strength, MPa | 260 to 710 | |
| 200 to 220 |
| Poisson's Ratio | 0.3 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 73 |
| Shear Strength, MPa | 510 to 1100 | |
| 330 to 360 |
| Tensile Strength: Ultimate (UTS), MPa | 780 to 1860 | |
| 520 to 590 |
| Tensile Strength: Yield (Proof), MPa | 380 to 1590 | |
| 290 to 330 |
Thermal Properties
| Melting Completion (Liquidus), °C | 1330 | |
| 1470 |
| Melting Onset (Solidus), °C | 1200 | |
| 1420 to 1430 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 470 |
| Thermal Conductivity, W/m-K | 48 | |
| 52 |
| Thermal Expansion, µm/m-K | 14 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 5.0 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 5.4 | |
| 8.2 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.3 | |
| 7.9 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 190 | |
| 90 to 95 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 360 to 3440 | |
| 220 to 290 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 26 to 62 | |
| 18 to 21 |
| Strength to Weight: Bending, points | 23 to 41 | |
| 18 to 20 |
| Thermal Diffusivity, mm2/s | 13 | |
| 14 |
| Thermal Shock Resistance, points | 19 to 46 | |
| 15 to 17 |