Nickel Beryllium 360 vs. EN 1.4310 Stainless Steel
Nickel beryllium 360 belongs to the nickel alloys classification, while EN 1.4310 stainless steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is nickel beryllium 360 and the bottom bar is EN 1.4310 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Elongation at Break, % | 1.0 to 30 | |
| 14 to 45 |
| Fatigue Strength, MPa | 260 to 710 | |
| 240 to 330 |
| Poisson's Ratio | 0.3 | |
| 0.28 |
| Shear Modulus, GPa | 77 | |
| 77 |
| Shear Strength, MPa | 510 to 1100 | |
| 510 to 550 |
| Tensile Strength: Ultimate (UTS), MPa | 780 to 1860 | |
| 730 to 900 |
| Tensile Strength: Yield (Proof), MPa | 380 to 1590 | |
| 260 to 570 |
Thermal Properties
| Melting Completion (Liquidus), °C | 1330 | |
| 1420 |
| Melting Onset (Solidus), °C | 1200 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 480 |
| Thermal Conductivity, W/m-K | 48 | |
| 15 |
| Thermal Expansion, µm/m-K | 14 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 5.0 | |
| 2.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 5.4 | |
| 2.7 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.3 | |
| 7.8 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 190 | |
| 110 to 260 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 360 to 3440 | |
| 170 to 830 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 26 to 62 | |
| 26 to 32 |
| Strength to Weight: Bending, points | 23 to 41 | |
| 23 to 27 |
| Thermal Diffusivity, mm2/s | 13 | |
| 4.0 |
| Thermal Shock Resistance, points | 19 to 46 | |
| 15 to 18 |