Nickel Beryllium 360 vs. CC383H Copper-nickel
Nickel beryllium 360 belongs to the nickel alloys classification, while CC383H copper-nickel belongs to the copper alloys. There are 22 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is nickel beryllium 360 and the bottom bar is CC383H copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 140 |
| Elongation at Break, % | 1.0 to 30 | |
| 20 |
| Poisson's Ratio | 0.3 | |
| 0.33 |
| Shear Modulus, GPa | 77 | |
| 52 |
| Tensile Strength: Ultimate (UTS), MPa | 780 to 1860 | |
| 490 |
| Tensile Strength: Yield (Proof), MPa | 380 to 1590 | |
| 260 |
Thermal Properties
| Melting Completion (Liquidus), °C | 1330 | |
| 1180 |
| Melting Onset (Solidus), °C | 1200 | |
| 1130 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 410 |
| Thermal Conductivity, W/m-K | 48 | |
| 29 |
| Thermal Expansion, µm/m-K | 14 | |
| 15 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 5.0 | |
| 5.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 5.4 | |
| 5.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.3 | |
| 8.9 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 190 | |
| 84 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 360 to 3440 | |
| 250 |
| Stiffness to Weight: Axial, points | 13 | |
| 8.6 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 26 to 62 | |
| 15 |
| Strength to Weight: Bending, points | 23 to 41 | |
| 16 |
| Thermal Diffusivity, mm2/s | 13 | |
| 8.1 |
| Thermal Shock Resistance, points | 19 to 46 | |
| 17 |