Nickel Beryllium 360 vs. Grade 28 Titanium
Nickel beryllium 360 belongs to the nickel alloys classification, while grade 28 titanium belongs to the titanium alloys. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is nickel beryllium 360 and the bottom bar is grade 28 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 110 |
| Elongation at Break, % | 1.0 to 30 | |
| 11 to 17 |
| Fatigue Strength, MPa | 260 to 710 | |
| 330 to 480 |
| Poisson's Ratio | 0.3 | |
| 0.32 |
| Shear Modulus, GPa | 77 | |
| 40 |
| Shear Strength, MPa | 510 to 1100 | |
| 420 to 590 |
| Tensile Strength: Ultimate (UTS), MPa | 780 to 1860 | |
| 690 to 980 |
| Tensile Strength: Yield (Proof), MPa | 380 to 1590 | |
| 540 to 810 |
Thermal Properties
| Melting Completion (Liquidus), °C | 1330 | |
| 1640 |
| Melting Onset (Solidus), °C | 1200 | |
| 1590 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 550 |
| Thermal Conductivity, W/m-K | 48 | |
| 8.3 |
| Thermal Expansion, µm/m-K | 14 | |
| 9.9 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 5.0 | |
| 1.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 5.4 | |
| 2.7 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.3 | |
| 4.5 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 190 | |
| 87 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 360 to 3440 | |
| 1370 to 3100 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 35 |
| Strength to Weight: Axial, points | 26 to 62 | |
| 43 to 61 |
| Strength to Weight: Bending, points | 23 to 41 | |
| 39 to 49 |
| Thermal Diffusivity, mm2/s | 13 | |
| 3.4 |
| Thermal Shock Resistance, points | 19 to 46 | |
| 47 to 66 |