Nickel Beryllium 360 vs. K93050 Alloy
Nickel beryllium 360 belongs to the nickel alloys classification, while K93050 alloy belongs to the iron alloys. There are 14 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is nickel beryllium 360 and the bottom bar is K93050 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Poisson's Ratio | 0.3 | |
| 0.3 |
| Shear Modulus, GPa | 77 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 780 to 1860 | |
| 500 to 680 |
Thermal Properties
| Melting Completion (Liquidus), °C | 1330 | |
| 1430 |
| Melting Onset (Solidus), °C | 1200 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 460 |
| Thermal Expansion, µm/m-K | 14 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.3 | |
| 8.2 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 23 |
| Strength to Weight: Axial, points | 26 to 62 | |
| 17 to 23 |
| Strength to Weight: Bending, points | 23 to 41 | |
| 17 to 21 |
| Thermal Shock Resistance, points | 19 to 46 | |
| 16 to 21 |