Nickel Beryllium 360 vs. R60705 Alloy
Nickel beryllium 360 belongs to the nickel alloys classification, while R60705 alloy belongs to the otherwise unclassified metals. There are 19 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is nickel beryllium 360 and the bottom bar is R60705 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 98 |
| Elongation at Break, % | 1.0 to 30 | |
| 18 |
| Fatigue Strength, MPa | 260 to 710 | |
| 290 |
| Poisson's Ratio | 0.3 | |
| 0.34 |
| Shear Modulus, GPa | 77 | |
| 37 |
| Tensile Strength: Ultimate (UTS), MPa | 780 to 1860 | |
| 540 |
| Tensile Strength: Yield (Proof), MPa | 380 to 1590 | |
| 430 |
Thermal Properties
| Specific Heat Capacity, J/kg-K | 460 | |
| 270 |
| Thermal Conductivity, W/m-K | 48 | |
| 17 |
| Thermal Expansion, µm/m-K | 14 | |
| 6.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.3 | |
| 6.7 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 190 | |
| 90 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 360 to 3440 | |
| 950 |
| Stiffness to Weight: Axial, points | 13 | |
| 8.1 |
| Stiffness to Weight: Bending, points | 24 | |
| 23 |
| Strength to Weight: Axial, points | 26 to 62 | |
| 22 |
| Strength to Weight: Bending, points | 23 to 41 | |
| 22 |
| Thermal Diffusivity, mm2/s | 13 | |
| 9.5 |
| Thermal Shock Resistance, points | 19 to 46 | |
| 63 |