Nuclear Grade Hafnium vs. C34200 Brass
Nuclear grade hafnium belongs to the otherwise unclassified metals classification, while C34200 brass belongs to the copper alloys. There are 17 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is nuclear grade hafnium and the bottom bar is C34200 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 78 | |
| 100 |
| Elongation at Break, % | 25 | |
| 3.0 to 17 |
| Poisson's Ratio | 0.26 | |
| 0.31 |
| Shear Modulus, GPa | 31 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 350 | |
| 370 to 650 |
| Tensile Strength: Yield (Proof), MPa | 170 | |
| 150 to 420 |
Thermal Properties
| Latent Heat of Fusion, J/g | 130 | |
| 170 |
| Specific Heat Capacity, J/kg-K | 140 | |
| 380 |
| Thermal Expansion, µm/m-K | 5.9 | |
| 21 |
Otherwise Unclassified Properties
| Density, g/cm3 | 13 | |
| 8.2 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 73 | |
| 9.0 to 98 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 | |
| 110 to 870 |
| Stiffness to Weight: Axial, points | 3.3 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 11 | |
| 19 |
| Strength to Weight: Axial, points | 7.4 | |
| 13 to 22 |
| Strength to Weight: Bending, points | 8.4 | |
| 14 to 20 |
| Thermal Shock Resistance, points | 55 | |
| 12 to 22 |
Alloy Composition
| Copper (Cu), % | 0 | |
| 62 to 65 |
| Hafnium (Hf), % | 99.8 to 100 | |
| 0 |
| Iron (Fe), % | 0 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 1.5 to 2.5 |
| Zinc (Zn), % | 0 | |
| 32 to 36.5 |
| Residuals, % | 0 | |
| 0 to 0.4 |