Nuclear Grade Hafnium vs. C41300 Brass
Nuclear grade hafnium belongs to the otherwise unclassified metals classification, while C41300 brass belongs to the copper alloys. There are 17 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is nuclear grade hafnium and the bottom bar is C41300 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 78 | |
| 110 |
| Elongation at Break, % | 25 | |
| 2.0 to 44 |
| Poisson's Ratio | 0.26 | |
| 0.33 |
| Shear Modulus, GPa | 31 | |
| 42 |
| Tensile Strength: Ultimate (UTS), MPa | 350 | |
| 300 to 630 |
| Tensile Strength: Yield (Proof), MPa | 170 | |
| 120 to 570 |
Thermal Properties
| Latent Heat of Fusion, J/g | 130 | |
| 200 |
| Specific Heat Capacity, J/kg-K | 140 | |
| 380 |
| Thermal Expansion, µm/m-K | 5.9 | |
| 18 |
Otherwise Unclassified Properties
| Density, g/cm3 | 13 | |
| 8.7 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 73 | |
| 11 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 | |
| 69 to 1440 |
| Stiffness to Weight: Axial, points | 3.3 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 11 | |
| 18 |
| Strength to Weight: Axial, points | 7.4 | |
| 9.6 to 20 |
| Strength to Weight: Bending, points | 8.4 | |
| 11 to 19 |
| Thermal Shock Resistance, points | 55 | |
| 11 to 22 |
Alloy Composition
| Copper (Cu), % | 0 | |
| 89 to 93 |
| Hafnium (Hf), % | 99.8 to 100 | |
| 0 |
| Iron (Fe), % | 0 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 | |
| 0 to 0.1 |
| Tin (Sn), % | 0 | |
| 0.7 to 1.3 |
| Zinc (Zn), % | 0 | |
| 5.1 to 10.3 |
| Residuals, % | 0 | |
| 0 to 0.5 |