Nuclear Grade Hafnium vs. C71000 Copper-nickel
Nuclear grade hafnium belongs to the otherwise unclassified metals classification, while C71000 copper-nickel belongs to the copper alloys. There are 13 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is nuclear grade hafnium and the bottom bar is C71000 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 78 | |
| 130 |
| Poisson's Ratio | 0.26 | |
| 0.33 |
| Shear Modulus, GPa | 31 | |
| 49 |
| Tensile Strength: Ultimate (UTS), MPa | 350 | |
| 320 to 560 |
Thermal Properties
| Latent Heat of Fusion, J/g | 130 | |
| 230 |
| Specific Heat Capacity, J/kg-K | 140 | |
| 400 |
| Thermal Expansion, µm/m-K | 5.9 | |
| 15 |
Otherwise Unclassified Properties
| Density, g/cm3 | 13 | |
| 8.9 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.3 | |
| 8.2 |
| Stiffness to Weight: Bending, points | 11 | |
| 19 |
| Strength to Weight: Axial, points | 7.4 | |
| 10 to 18 |
| Strength to Weight: Bending, points | 8.4 | |
| 12 to 17 |
| Thermal Shock Resistance, points | 55 | |
| 12 to 20 |
Alloy Composition
| Copper (Cu), % | 0 | |
| 73.5 to 80.5 |
| Hafnium (Hf), % | 99.8 to 100 | |
| 0 |
| Iron (Fe), % | 0 | |
| 0.5 to 1.0 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 0 | |
| 19 to 23 |
| Zinc (Zn), % | 0 | |
| 0 to 1.0 |
| Residuals, % | 0 | |
| 0 to 0.5 |