PFA vs. CPVC

Both PFA and CPVC are thermoplastics. There are 17 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is PFA and the bottom bar is CPVC.

Perfluoroalkoxy (PFA)Chlorinated Polyvinyl Chloride (CPVC, PVC-C)

Metric UnitsUS Customary Units

Mechanical Properties

Elongation at Break, %		300
Elongation at Break, %		4.0

Flexural Modulus, GPa		0.7
Flexural Modulus, GPa		2.5

Tensile Strength: Ultimate (UTS), MPa		30
Tensile Strength: Ultimate (UTS), MPa		50

Thermal Properties

Heat Deflection Temperature At 1.82 MPa (264 psi), °C		50
Heat Deflection Temperature At 1.82 MPa (264 psi), °C		91

Maximum Temperature: Mechanical, °C		260
Maximum Temperature: Mechanical, °C		80

Specific Heat Capacity, J/kg-K		1000
Specific Heat Capacity, J/kg-K		780

Thermal Conductivity, W/m-K		0.25
Thermal Conductivity, W/m-K		0.31

Thermal Expansion, µm/m-K		120
Thermal Expansion, µm/m-K		65

Electrical Properties

Dielectric Constant (Relative Permittivity) At 1 Hz		2.1
Dielectric Constant (Relative Permittivity) At 1 Hz		3.7

Dielectric Strength (Breakdown Potential), kV/mm		22
Dielectric Strength (Breakdown Potential), kV/mm		49

Electrical Resistivity Order of Magnitude, 10^x Ω-m		16
Electrical Resistivity Order of Magnitude, 10^x Ω-m		13

Otherwise Unclassified Properties

Density, g/cm³		2.2
Density, g/cm³		1.5

Limiting Oxygen Index (LOI), %		80
Limiting Oxygen Index (LOI), %		57

Water Absorption After 24 Hours, %		0
Water Absorption After 24 Hours, %		0.030

Common Calculations

Strength to Weight: Axial, points		3.9
Strength to Weight: Axial, points		9.4

Strength to Weight: Bending, points		10
Strength to Weight: Bending, points		20

Thermal Diffusivity, mm²/s		0.12
Thermal Diffusivity, mm²/s		0.27