PVC-P vs. NEMA Laminate
PVC-P belongs to the thermoplastics classification, while NEMA laminate belongs to the thermoset plastics. There are 9 material properties with values for both materials. Properties with values for just one material (23, in this case) are not shown.
For each property being compared, the top bar is PVC-P and the bottom bar is NEMA laminate.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.4 | |
| 1.3 to 1.9 |
| Dielectric Strength (Breakdown Potential), kV/mm | 20 | |
| 12 to 21 |
| Impact Strength: Notched Izod, J/m | 550 | |
| 20 to 430 |
| Maximum Temperature: Mechanical, °C | 75 | |
| 120 to 200 |
| Strength to Weight: Axial, points | 3.2 | |
| 8.3 to 40 |
| Strength to Weight: Bending, points | 10 | |
| 17 to 50 |
| Tensile Strength: Ultimate (UTS), MPa | 16 | |
| 55 to 260 |
| Thermal Expansion, µm/m-K | 160 | |
| 9.0 to 20 |
| Water Absorption After 24 Hours, % | 0.45 | |
| 0.17 to 3.5 |