PVC-P vs. PA 6
Both PVC-P and PA 6 are thermoplastics. There are 9 material properties with values for both materials. Properties with values for just one material (21, in this case) are not shown.
For each property being compared, the top bar is PVC-P and the bottom bar is PA 6.
Metric UnitsUS Customary Units
Material Properties
| Dielectric Strength (Breakdown Potential), kV/mm | 20 | |
| 10 to 30 |
| Elastic (Young's, Tensile) Modulus, GPa | 1.4 | |
| 1.1 to 16 |
| Elongation at Break, % | 180 | |
| 2.5 to 67 |
| Glass Transition Temperature, °C | 75 | |
| 40 |
| Limiting Oxygen Index (LOI), % | 44 | |
| 24 |
| Maximum Temperature: Autoignition, °C | 320 | |
| 430 |
| Maximum Temperature: Decomposition, °C | 250 | |
| 430 |
| Melting Onset (Solidus), °C | 190 | |
| 230 |
| Tensile Strength: Ultimate (UTS), MPa | 16 | |
| 35 to 210 |