PAI vs. NEMA Laminate
PAI belongs to the thermoplastics classification, while NEMA laminate belongs to the thermoset plastics. There are 11 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is PAI and the bottom bar is NEMA laminate.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 260 to 300 | |
| 190 to 360 |
| Flexural Modulus, GPa | 4.0 to 6.8 | |
| 6.4 to 18 |
| Flexural Strength, MPa | 160 to 320 | |
| 87 to 340 |
| Impact Strength: Notched Izod, J/m | 45 to 140 | |
| 20 to 430 |
| Tensile Strength: Ultimate (UTS), MPa | 100 to 180 | |
| 55 to 260 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 260 | |
| 120 to 200 |
| Thermal Expansion, µm/m-K | 15 to 34 | |
| 9.0 to 20 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.4 to 1.6 | |
| 1.3 to 1.9 |
| Water Absorption After 24 Hours, % | 0.3 to 0.4 | |
| 0.17 to 3.5 |
Common Calculations
| Strength to Weight: Axial, points | 19 to 34 | |
| 8.3 to 40 |
| Strength to Weight: Bending, points | 33 to 49 | |
| 17 to 50 |