PAI vs. PMMA
Both PAI and PMMA are thermoplastics. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is PAI and the bottom bar is PMMA.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 260 to 300 | |
| 120 |
| Elastic (Young's, Tensile) Modulus, GPa | 4.0 to 8.3 | |
| 3.2 |
| Elongation at Break, % | 3.0 to 12 | |
| 4.0 |
| Flexural Strength, MPa | 160 to 320 | |
| 110 |
| Impact Strength: Notched Izod, J/m | 45 to 140 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 100 to 180 | |
| 71 |
Thermal Properties
| Glass Transition Temperature, °C | 280 | |
| 110 |
| Heat Deflection Temperature At 1.82 MPa (264 psi), °C | 280 | |
| 96 |
| Maximum Temperature: Autoignition, °C | 530 | |
| 320 |
| Maximum Temperature: Decomposition, °C | 490 | |
| 360 |
| Specific Heat Capacity, J/kg-K | 910 to 1000 | |
| 1260 |
| Thermal Conductivity, W/m-K | 0.26 to 0.53 | |
| 0.19 |
| Thermal Expansion, µm/m-K | 15 to 34 | |
| 76 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.4 to 1.6 | |
| 1.2 |
| Limiting Oxygen Index (LOI), % | 45 | |
| 17 |
Common Calculations
| Stiffness to Weight: Axial, points | 1.6 to 3.2 | |
| 1.5 |
| Stiffness to Weight: Bending, points | 38 to 47 | |
| 42 |
| Strength to Weight: Axial, points | 19 to 34 | |
| 17 |
| Strength to Weight: Bending, points | 33 to 49 | |
| 32 |
| Thermal Diffusivity, mm2/s | 0.16 to 0.41 | |
| 0.13 |
| Thermal Shock Resistance, points | 48 to 110 | |
| 21 |