PA 11 vs. PAS
Both PA 11 and PAS are thermoplastics. There are 9 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.
For each property being compared, the top bar is PA 11 and the bottom bar is PAS.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.0 | |
| 1.4 |
| Elastic (Young's, Tensile) Modulus, GPa | 0.4 to 1.3 | |
| 2.7 |
| Elongation at Break, % | 80 to 130 | |
| 40 |
| Limiting Oxygen Index (LOI), % | 29 | |
| 33 |
| Stiffness to Weight: Axial, points | 0.22 to 0.71 | |
| 1.1 |
| Stiffness to Weight: Bending, points | 24 to 36 | |
| 34 |
| Strength to Weight: Axial, points | 6.7 to 14 | |
| 17 |
| Strength to Weight: Bending, points | 18 to 30 | |
| 31 |
| Tensile Strength: Ultimate (UTS), MPa | 25 to 51 | |
| 83 |