PA 6/10 vs. POM-H
Both PA 6/10 and POM-H are thermoplastics. There are 8 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is PA 6/10 and the bottom bar is POM-H.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.1 | |
| 1.4 to 1.6 |
| Elongation at Break, % | 110 to 120 | |
| 7.0 to 55 |
| Flexural Modulus, GPa | 1.4 to 2.0 | |
| 2.9 to 4.3 |
| Impact Strength: Notched Izod, J/m | 85 | |
| 40 to 75 |
| Specific Heat Capacity, J/kg-K | 1510 | |
| 1250 to 1460 |
| Strength to Weight: Axial, points | 11 to 15 | |
| 11 to 13 |
| Strength to Weight: Bending, points | 25 to 30 | |
| 22 to 26 |
| Tensile Strength: Ultimate (UTS), MPa | 45 to 60 | |
| 60 to 67 |