PA 6/10 vs. COC
Both PA 6/10 and COC are thermoplastics. There are 9 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is PA 6/10 and the bottom bar is COC.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.1 | |
| 1.0 |
| Elastic (Young's, Tensile) Modulus, GPa | 1.6 to 2.3 | |
| 3.0 |
| Elongation at Break, % | 110 to 120 | |
| 2.5 |
| Stiffness to Weight: Axial, points | 0.78 to 1.1 | |
| 1.7 |
| Stiffness to Weight: Bending, points | 34 to 39 | |
| 48 |
| Strength to Weight: Axial, points | 11 to 15 | |
| 17 |
| Strength to Weight: Bending, points | 25 to 30 | |
| 34 |
| Tensile Strength: Ultimate (UTS), MPa | 45 to 60 | |
| 60 |
| Water Absorption After 24 Hours, % | 0.26 | |
| 0 |