PA 6/10 vs. PHB
Both PA 6/10 and PHB are thermoplastics. There are 13 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is PA 6/10 and the bottom bar is PHB.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 1.6 to 2.3 | |
1.3 |
Elongation at Break, % | 110 to 120 | |
7.5 |
Flexural Strength, MPa | 48 to 59 | |
20 |
Tensile Strength: Ultimate (UTS), MPa | 45 to 60 | |
30 |
Thermal Properties
Maximum Temperature: Mechanical, °C | 80 | |
120 |
Melting Onset (Solidus), °C | 220 | |
180 |
Electrical Properties
Dielectric Constant (Relative Permittivity) At 1 Hz | 3.9 to 12 | |
3.0 |
Otherwise Unclassified Properties
Density, g/cm3 | 1.1 | |
1.3 |
Water Absorption After 24 Hours, % | 0.26 | |
0.75 |
Common Calculations
Stiffness to Weight: Axial, points | 0.78 to 1.1 | |
0.58 |
Stiffness to Weight: Bending, points | 34 to 39 | |
29 |
Strength to Weight: Axial, points | 11 to 15 | |
6.7 |
Strength to Weight: Bending, points | 25 to 30 | |
17 |