PA 6/10 vs. PTT
Both PA 6/10 and PTT are thermoplastics. There are 11 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is PA 6/10 and the bottom bar is PTT.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 1.6 to 2.3 | |
| 2.5 |
| Elongation at Break, % | 110 to 120 | |
| 60 |
| Flexural Modulus, GPa | 1.4 to 2.0 | |
| 2.8 |
| Flexural Strength, MPa | 48 to 59 | |
| 100 |
| Tensile Strength: Ultimate (UTS), MPa | 45 to 60 | |
| 60 |
Thermal Properties
| Melting Onset (Solidus), °C | 220 | |
| 230 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.1 | |
| 1.3 |
Common Calculations
| Stiffness to Weight: Axial, points | 0.78 to 1.1 | |
| 1.0 |
| Stiffness to Weight: Bending, points | 34 to 39 | |
| 34 |
| Strength to Weight: Axial, points | 11 to 15 | |
| 13 |
| Strength to Weight: Bending, points | 25 to 30 | |
| 26 |