PA 6/10 vs. UPVC
Both PA 6/10 and uPVC are thermoplastics. There are 21 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is PA 6/10 and the bottom bar is uPVC.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 1.6 to 2.3 | |
| 3.7 |
| Elongation at Break, % | 110 to 120 | |
| 58 |
| Flexural Modulus, GPa | 1.4 to 2.0 | |
| 3.5 |
| Flexural Strength, MPa | 48 to 59 | |
| 80 |
| Impact Strength: Notched Izod, J/m | 85 | |
| 360 |
| Tensile Strength: Ultimate (UTS), MPa | 45 to 60 | |
| 47 |
Thermal Properties
| Maximum Temperature: Decomposition, °C | 440 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 80 | |
| 95 |
| Melting Onset (Solidus), °C | 220 | |
| 180 |
| Specific Heat Capacity, J/kg-K | 1510 | |
| 880 |
| Thermal Conductivity, W/m-K | 0.23 | |
| 0.16 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 Hz | 3.9 to 12 | |
| 3.4 |
| Dielectric Strength (Breakdown Potential), kV/mm | 15 to 19 | |
| 19 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.1 | |
| 1.4 |
| Limiting Oxygen Index (LOI), % | 25 | |
| 42 |
| Water Absorption After 24 Hours, % | 0.26 | |
| 0.24 |
Common Calculations
| Stiffness to Weight: Axial, points | 0.78 to 1.1 | |
| 1.5 |
| Stiffness to Weight: Bending, points | 34 to 39 | |
| 37 |
| Strength to Weight: Axial, points | 11 to 15 | |
| 9.1 |
| Strength to Weight: Bending, points | 25 to 30 | |
| 20 |
| Thermal Diffusivity, mm2/s | 0.13 | |
| 0.13 |