PA 6 vs. ETFE
Both PA 6 and ETFE are thermoplastics. There are 10 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.
For each property being compared, the top bar is PA 6 and the bottom bar is ETFE.
Metric UnitsUS Customary Units
Material Properties
| Dielectric Constant (Relative Permittivity) At 1 MHz | 3.3 to 5.0 | |
| 2.6 |
| Dielectric Strength (Breakdown Potential), kV/mm | 10 to 30 | |
| 16 |
| Elastic (Young's, Tensile) Modulus, GPa | 1.1 to 16 | |
| 1.5 |
| Elongation at Break, % | 2.5 to 67 | |
| 230 |
| Flexural Modulus, GPa | 1.2 to 14 | |
| 1.2 |
| Limiting Oxygen Index (LOI), % | 24 | |
| 30 |
| Maximum Temperature: Autoignition, °C | 430 | |
| 540 |
| Maximum Temperature: Decomposition, °C | 430 | |
| 400 |
| Melting Onset (Solidus), °C | 230 | |
| 260 |
| Tensile Strength: Ultimate (UTS), MPa | 35 to 210 | |
| 46 |