PA 6 vs. PBI
PA 6 belongs to the thermoplastics classification, while PBI belongs to the thermoset plastics. There are 10 material properties with values for both materials. Properties with values for just one material (20, in this case) are not shown.
For each property being compared, the top bar is PA 6 and the bottom bar is PBI.
Metric UnitsUS Customary Units
Material Properties
| Dielectric Constant (Relative Permittivity) At 1 MHz | 3.3 to 5.0 | |
| 3.8 |
| Dielectric Strength (Breakdown Potential), kV/mm | 10 to 30 | |
| 23 |
| Elastic (Young's, Tensile) Modulus, GPa | 1.1 to 16 | |
| 5.9 |
| Elongation at Break, % | 2.5 to 67 | |
| 3.0 |
| Flexural Modulus, GPa | 1.2 to 14 | |
| 6.5 |
| Flexural Strength, MPa | 40 to 230 | |
| 220 |
| Glass Transition Temperature, °C | 40 | |
| 410 |
| Limiting Oxygen Index (LOI), % | 24 | |
| 58 |
| Maximum Temperature: Decomposition, °C | 430 | |
| 590 |
| Tensile Strength: Ultimate (UTS), MPa | 35 to 210 | |
| 160 |