PAR vs. PVC-P
Both PAR and PVC-P are thermoplastics. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is PAR and the bottom bar is PVC-P.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 2.0 | |
| 1.4 |
| Elongation at Break, % | 50 | |
| 180 |
| Impact Strength: Notched Izod, J/m | 220 | |
| 550 |
| Tensile Strength: Ultimate (UTS), MPa | 67 | |
| 16 |
Thermal Properties
| Glass Transition Temperature, °C | 190 | |
| 75 |
| Maximum Temperature: Decomposition, °C | 470 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 1200 | |
| 1400 |
| Thermal Conductivity, W/m-K | 0.18 | |
| 0.17 |
| Thermal Expansion, µm/m-K | 88 | |
| 160 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 Hz | 3.0 | |
| 5.8 |
| Dielectric Strength (Breakdown Potential), kV/mm | 16 | |
| 20 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 12 | |
| 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.2 | |
| 1.4 |
| Limiting Oxygen Index (LOI), % | 35 | |
| 44 |
| Water Absorption After 24 Hours, % | 0.26 | |
| 0.45 |
Common Calculations
| Stiffness to Weight: Axial, points | 0.93 | |
| 0.57 |
| Stiffness to Weight: Bending, points | 35 | |
| 28 |
| Strength to Weight: Axial, points | 16 | |
| 3.2 |
| Strength to Weight: Bending, points | 31 | |
| 10 |
| Thermal Diffusivity, mm2/s | 0.13 | |
| 0.090 |
| Thermal Shock Resistance, points | 27 | |
| 4.9 |