PAS vs. POM-C
Both PAS and POM-C are thermoplastics. There are 12 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is PAS and the bottom bar is POM-C.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 2.7 | |
| 2.8 to 9.7 |
| Elongation at Break, % | 40 | |
| 3.0 to 65 |
| Flexural Modulus, GPa | 2.8 | |
| 2.6 to 9.0 |
| Flexural Strength, MPa | 110 | |
| 83 to 170 |
| Impact Strength: Notched Izod, J/m | 85 | |
| 68 to 69 |
| Tensile Strength: Ultimate (UTS), MPa | 83 | |
| 61 to 110 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.4 | |
| 1.4 to 1.6 |
| Limiting Oxygen Index (LOI), % | 33 | |
| 15 |
Common Calculations
| Stiffness to Weight: Axial, points | 1.1 | |
| 1.1 to 3.3 |
| Stiffness to Weight: Bending, points | 34 | |
| 33 to 44 |
| Strength to Weight: Axial, points | 17 | |
| 12 to 19 |
| Strength to Weight: Bending, points | 31 | |
| 24 to 32 |