PCL vs. PETG
Both PCL and PETG are thermoplastics. There are 9 material properties with values for both materials. Properties with values for just one material (21, in this case) are not shown.
For each property being compared, the top bar is PCL and the bottom bar is PETG.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.1 | |
| 1.3 |
| Elastic (Young's, Tensile) Modulus, GPa | 1.2 | |
| 2.2 |
| Glass Transition Temperature, °C | -60 | |
| 81 |
| Melting Onset (Solidus), °C | 60 | |
| 140 |
| Stiffness to Weight: Axial, points | 0.61 | |
| 1.0 |
| Stiffness to Weight: Bending, points | 32 | |
| 34 |
| Strength to Weight: Axial, points | 2.5 | |
| 12 |
| Strength to Weight: Bending, points | 9.4 | |
| 25 |
| Tensile Strength: Ultimate (UTS), MPa | 10 | |
| 53 |